Itme No.

Powder Type & Composition

Particle Size（um）

Properties & Industrial Application

BS706-001

Cr2O3≥99.5%

Fused and Crushed

-74/+38um

-45/+15um

-30/+10um

APS;Tough, dense and smooth, high hardness, excellent resistance to sliding and abrasive wear, erosion, cavitation and corrosion; Coatings are insoluble in acids, alkalis and alcohol; Used as hard face wear, fibre abrasion, particle erosion, gas and liquid corrosion-resistant coatings; Used on pump seal areas,grounds,rolls and wear rings.

BS706-005

Cr2O3≥99.95%

Sintered and Crushed

-74/+38um

-45/+15um

-30/+10um

APS; Tough, dense and smooth, high hardness, excellent resistance to sliding and abrasive wear,erosion,cavitation and corrosion; Coatings are insoluble in acids, alkalis and alcohol; Used as hard face wear, fibre abrasion, particle erosion, gas and liquid corrosion-resistant coatings; Used on anilox roller, roller of printing machines, dynamic and static ring

BS706-002

Cr2O3≥99.95%

Agglomerated and Sintered

-74/+38um

-45/+15um

-30/+10um

APS; Tough, dense and smooth, high hardness, excellent resistance to sliding and abrasive wear,erosion,cavitation and corrosion; Coatings are insoluble in acids, alkalis and alcohol; Used as hard face wear, fibre abrasion, particle erosion, gas and liquid corrosion-resistant coatings; Used on pump seal areas, grounds, rolls and wear rings.

BS736-002

Cr2O3-3TiO2-5SiO2

Agglomerated and Sintered

-74/+38um

-45/+15um

-30/+10um

APS; Tough, dense and smooth, high hardness, excellent resistance to sliding and abrasive wear, erosion, cavitation and corrosion; Coatings are insoluble in acids, alkalis and alcohol; Good friction characteristics; Used as hard face wear, fiber abrasion, particle erosion, gas and liquid corrosion-resistant coatings; Used on pump seal areas, grounds, rolls and wear rings.

BS702-002

TiO2≥99.7%

Agglomerated and Sintered

-45/+15um

APS; Tough and dense, high bonding strength, protection against high temperature oxidation, resistant to wear by abrasive grains and hard surfaces;

Moderate abrasive wear resistance; Soluble in alkalis and sulfuric acid, but resistant to attack in many other environments; Slightly conductive, static electricity does not build up on the coating surface.

BS702-005

TiO2≥99.7%

Sintered and Crushed

-45/+15um

APS; Tough and dense, high bonding strength,protection against high temperature oxidation, resistant to wear by abrasive grains and hard surfaces;

Moderate abrasive wear resistance; Soluble in alkalis and sulfuric acid, but resistant to attack in many other environments; Slightly conductive, static electricity does not build up on the coating surface.

BS701-001

Al2O3≥99.5%

 Fused and Crushed

-74/+38um

-45/+15um

-30/+10um

APS; High hardness, excellent resistance to abrasive and sliding wear, erosion, cavitation and corrosion; High dielectric strength, service temperatures:1650 °C(3000 °F); Used as hard face wear, fibre abrasion; Particle erosion and high temperature erosion resistant coatings.

BS701-002

Al2O3≥99.95%

Agglomerated and Sintered

-74/+38um

-45/+15um

-30/+10um

APS; Excellent insulation and thermal insulation characteristics;

Wear resistant, chemically inert, stable under high temperature conditions; For electronic and semiconductor production tools, biomedical implants;

Operating temperature up to 1650 °C (3000 °F).

BS701-001

  Al2O3 -3TiO2

 Fused and Crushed

-74/+38um

-45/+15um

-30/+10um

APS; Coatings are smooth and dense; For use as corrosion, abrasion, erosion and sliding wear resistant coatings; Typical applications in textile machines for guiding and handling of thread,rolls in paper industry,etc.; Good dielectric strength at room temperatures, lower dielectric strength than pure Al2O3 coatings.

BS701-002

  Al2O3 -3TiO2

 Agglomerated and Sintered

-74/+38um

-45/+15um

-30/+10um

APS; Coatings are smooth and dense; For use as corrosion, abrasion, erosion and sliding wear resistant coatings; Typical applications in textile machines for guiding and handling of thread,rolls in paper industry,etc.; Good dielectric strength at room temperatures, lower dielectric strength than pure Al2O3 coatings.

BS804-002

 ZrO2-8Y2O3

Agglomerated and Sintered

-90/+45um

-45/+15um

-40/+10um

APS; Coatings exhibit good chemical and thermal stability. Tough and dense, excellent resistance to thermal shock and particle erosion at high temperature, good insulation; Used as thermal barrier coatings for turbine combustion liners and airfoils; Hot gas corrosion protective coatings.

BS801-002

ZrO2-5CaO

Agglomerated and Sintered

-90/+45um

-45/+15um

-40/+10um

APS; Porous coat having good thermal insulation properties, resistant to corrosion, heat and thermal shock; Used for thermal barrier and gas corrosion resistant coatings.