Itme No.

Powder Type & Composition

Particle Size（um）

Properties & Industrial Application

BS941-003

Ni-5Al

Gas Atomized

-96/+45um

-53/+15um

APS,HVOF; Dense, machinable oxidation resistant and abrasion resistant coatings; Self-bonding;Bond coat for thermal sprayed ceramic and abradable materials;Service up to 800°C.

BS943-003

Ni-20Cr

Gas Atomized

-96/+45um

-53/+15um

APS,HVOF; Resists hot oxidizing and corrosive gases; Good bond coat for ceramic top coats; Chromium enhances corrosion resistance; Service up to 980°C.

BS944-003

Ni-18Cr-6Al

Gas Atomized

-96/+45um

-53/+15um

Self-bonding when plasma sprayed; Resists oxidation and corrosion at high temperatures; Service up to 980°C.

BS961-003

Ni-17Cr-6Al-0.5Y

Gas Atomized

-96/+45um

-53/+15um

Stable at high temperatures in hot corrosive or oxidizing environments. Used on turbine blades, etc.

BS962-003

Ni-18Cr-5Co-5Al-1Y

Gas Atomized

-96/+45um

-53/+15um

Max operating temperature 850°C; Stable at high temperatures in hot corrosive or oxidizing environments. Used on turbine blades, etc.

BS987-003

Ni-5Al-5Mo

Gas Atomized

-96/+45um

-53/+15um

Prepare self-adhesive, general purpose hard coatings for bearing applications; Tough, good corrosion and impact resistance; For machine parts, bearing housings, valves.

BS984-003

Ni-9Cr-7Al-5Mo-5Fe

Gas Atomized

-96/+45um

-53/+15um

APS; High hardness, excellent resistance to abrasive and sliding wear, erosion, cavitation and corrosion; High dielectric strength, service temperatures:1650 °C(3000 °F); Used as hard face wear, fibre abrasion; Particle erosion and high temperature erosion resistant coatings.

BS984-003

Ni-9Cr-7Al-5Mo-5Fe

Gas Atomized

-96/+45um

-53/+15um

Self-adhesive; Moderate wear and abrasion and corrosion resistance; Good machinability; For remediation and fabrication of carbon and corrosion resistant steels or as a bond coat; Operating temperature up to 760°C(1400°F).

BS113-003

 Ni-13Cr-2.5B-3Si-10Fe-0.45C

Gas Atomized

-105/+45um

-53/+15um

HRC40-50,the working temperature: 650°C; Moderate hardness,good toughness,good corrosion resistance, good friction between metal resistance and wettability; For oxyacetylene flame spray welding and laser cladding technique; Used for axial,glass mould,spray welding on the surface of the plunger, valve seat; Used for corrosion resistant coating on the surface of the axle.

BS113-004

Ni-13Cr-2.5B-3Si-10Fe-0.45C

Water Atomized

-105/+45um

-53/+15um

HRC40-50,the working temperature: 650°C; Moderate hardness,good toughness,good corrosion resistance, good friction between metal resistance and wettability; For oxyacetylene flame spray welding and laser cladding technique; Used for axial,glass mould,spray welding on the surface of the plunger, valve seat; Used for corrosion resistant coating on the surface of the axle.

BS115-003

 Ni-15Cr-3B-3Si-10Fe-0.75C

Gas Atomized

-105/+45um

-53/+15um

HRC53-58,working temperature:650°C;With high hardness and low coefficient of friction,between metal wear resistant performance is good,good crack resistance; For oxyacetylene spray welding, induction remelting, laser cladding process; Oil well pump plunger, sleeve and other hard surface wear and abrasive wear parts repair or protection.

BS115-004

Ni-15Cr-3B-3Si-10Fe-0.75C

Water Atomized

-105/+45um

-53/+15um

HRC53-58,working temperature:650°C;With high hardness and low coefficient of friction,between metal wear resistant performance is good,good crack resistance; For oxyacetylene spray welding, induction remelting, laser cladding process; Oil well pump plunger, sleeve and other hard surface wear and abrasive wear parts repair or protection.